High quality Rare Earth oxides products supplier

Brief information of Yttrium Fluoride

Appearance: White powder

Main content: 99.%-99.999%

CAS No: 13709-49-4

Density: 5.01 g/cm3

Stability: Insoluble in water, moderately

Molecular Weight: 225.81

Melting point:: 1387 °C

Specification

SEM

Application

The Y2O3 coating was strongly fluorinated under the plasma, and the thickness of the fluorinated layer was increased up to a few hundred nm with bias voltage. XPS analysis also confirmed a significant Y–F bonding on the surface and showed fluorine content at a maximum on the surface, decreasing with the depth from the surface. The etch rate increased with bias voltage and it was slightly higher in YF3 coating, implying that the etch rate depends on the surface fluorination and its removal by incident ions. Without applying bias voltage, the chemical reaction with the fluorocarbon plasma dominated, resulting in the formation of fine fluoride particles on the Y2O3 surface, but the YF3 coating was intact and clean for the same condition.These results indicate that the YF3 coating is a new plasma-facing material that produces fewer contamination particles.